Modificación de tejido de poliéster mediante la fabricación de compuestos de nano-cobre
DOI:
https://doi.org/10.15649/2346075X.1005Palabras clave:
In situ synthesis, nano-plates copper, polyester fabric, cetyltrimethylammonium bromide (CTAB)Resumen
This research introduces a new method of polyester fabric surface modification in order to achieve distinctive features. The copper sulfate, sodium hydroxide and cetyl trimethylammonium bromide (CTAB) were used to synthesize copper nanoparticles, and loaded on the polyester fabric surface. The optimal sample was considered by SEM-EDX, FT-IR and XRD devices. SEM images showed copper nanoparticles in shape of nano-plates with 150 to 600 nm in length and thickness of about 30 nm. The best results obtained on the modified fabric processed at boil for 120 min. According to the results of experiments CuO and Cu0 were synthesized on the fabric.
Licencia
Todos los artículos publicados en esta revista científica están protegidos por los derechos de autor. Los autores retienen los derechos de autor y conceden a la revista el derecho de primera publicación con el trabajo simultáneamente licenciado bajo una Licencia Creative Commons Atribución-NoComercial 4.0 Internacional (CC BY-NC 4.0) que permite compartir el trabajo con reconocimiento de autoría y sin fines comerciales.
Los lectores pueden copiar y distribuir el material de este número de la revista para fines no comerciales en cualquier medio, siempre que se cite el trabajo original y se den crédito a los autores y a la revista.
Cualquier uso comercial del material de esta revista está estrictamente prohibido sin el permiso por escrito del titular de los derechos de autor.
Para obtener más información sobre los derechos de autor de la revista y las políticas de acceso abierto, por favor visite nuestro sitio web.
Descargas