Modificación de tejido de poliéster mediante la fabricación de compuestos de nano-cobre

  • Mohammad Mahdi Jolaei Islamic Azad University
  • Majid Montazer Amirkabir University of Technology
  • Abo-Saeed Rashidi Islamic Azad University
  • Mohammad Bameni Moghadam Allameh Tabataba’i University
Palabras clave: In situ synthesis, nano-plates copper, polyester fabric, cetyltrimethylammonium bromide (CTAB)

Resumen

This research introduces a new method of polyester fabric surface modification in order to achieve distinctive features. The copper sulfate, sodium hydroxide and cetyl trimethylammonium bromide (CTAB) were used to synthesize copper nanoparticles, and loaded on the polyester fabric surface. The optimal sample was considered by SEM-EDX, FT-IR and XRD devices. SEM images showed copper nanoparticles in shape of nano-plates with 150 to 600 nm in length and thickness of about 30 nm. The best results obtained on the modified fabric processed at boil for 120 min. According to the results of experiments CuO and Cu0 were synthesized on the fabric.

Biografía del autor/a

Mohammad Mahdi Jolaei, Islamic Azad University

Department of Textile Engineering, Science and Research Branch, Islamic Azad University, Tehran, Iran

Majid Montazer, Amirkabir University of Technology

Department of Textile Engineering, Amirkabir University of Technology, Tehran, Iran

Abo-Saeed Rashidi, Islamic Azad University

Department of Textile Engineering, Science and Research Branch, Islamic Azad University, Tehran, Iran

Mohammad Bameni Moghadam, Allameh Tabataba’i University

Department of Statistics, Allameh Tabataba’i University, Tehran, Iran

Citas

E. Halevas and A. Pantazaki, "Copper Nanoparticles as Therapeutic Anticancer Agents," vol. 2, no. 1, p. 119, 2018.

S. Chandra, A. Kumar, and P. K. Tomar, "Synthesis and characterization of copper nanoparticles by reducing agent," J. Saudi Chem. Soc., vol. 18, no. 2, pp. 149-153, Apr. 2014.
https://doi.org/10.1016/j.jscs.2011.06.009

S. A. Patil, C.-H. Ryu, and H.-S. Kim, "Synthesis and Characterization of Copper Nanoparticles (Cu-Nps) using Rongalite as Reducing Agent and Photonic Sintering of Cu-Nps Ink for Printed Electronics," Int. J. Precis. Eng. Manuf. Technol., vol. 5, no. 2, pp. 239-245, Apr. 2018.
https://doi.org/10.1007/s40684-018-0024-7

Q. ZHANG, Z. YANG, B. DING, X. LAN, and Y. GUO, "Preparation of copper nanoparticles by chemical reduction method using potassium borohydride," Trans. Nonferrous Met. Soc. China, vol. 20, pp. s240-s244, May 2010.
https://doi.org/10.1016/S1003-6326(10)60047-7

A. Umer, S. Naveed, N. Ramzan, M. S. Rafique, and M. Imran, "A green method for the synthesis of copper nanoparticles using l-ascorbic acid," Rev. Mater., 2014.
https://doi.org/10.1590/S1517-70762014000300002

S. Shahidi, J. Wiener, and M. Ghoranneviss, "Surface Modification Methods for Improving the Dyeability of Textile Fabrics," in Eco-Friendly Textile Dyeing and Finishing, InTech, 2013.
https://doi.org/10.5772/53911

A. B. Rezaie and M. Montazer, "Polyester modification through synthesis of copper nanoparticles in presence of triethanolamine optimized with response surface methodology," Fibers Polym., vol. 18, no. 3, pp. 434-444, Mar. 2017.
https://doi.org/10.1007/s12221-017-6780-0

M. Abdulla-Al-Mamun, Y. Kusumoto, and M. Muruganandham, "Simple new synthesis of copper nanoparticles in water/acetonitrile mixed solvent and their characterization," Mater. Lett., vol. 63, no. 23, pp. 2007-2009, Sep. 2009.
https://doi.org/10.1016/j.matlet.2009.06.037

B. H. Chattopadhyay, Patel, "Effect of nanosized colloidal copper on cotton fabric," J. Eng. Fabr. Fibers, vol. 5, no. 3, pp. 1-6, 2010.
https://doi.org/10.1177/155892501000500301

M. M. Jolaei, M. Montazer, A. Rashidi, and M. B. Moghadam, "Usage of alkaline glucose for Synthesis Copper Nano particle on Polyester Fabric," Ciência e Nat., vol. 37, p. 63, Dec. 2015.
https://doi.org/10.5902/2179460X20831

M. Montazer and M. M. Jolaei, "Novel spacer three-dimensional polyester fabric with β -cyclodextrin and butane tetra carboxylic acid," J. Text. Inst., vol. 101, no. 2, pp. 165-172, Feb. 2010.
https://doi.org/10.1080/00405000802309592

M. Montazer and M. M. Jolaei, "Î2-Cyclodextrin stabilized on three-dimensional polyester fabric with different crosslinking agents," J. Appl. Polym. Sci., vol. 116, no. 1, pp. 210-217, Apr. 2010.
https://doi.org/10.1002/app.31175

M. M. Jolaei, "Improvement of 3D Polyester Fabric Surface with Nano Beta-Cyclodextrin and Hydrophilic Silicone and Microemulsion Softeners," International Journal of Advanced Biotechnology and Research (IJBR), vol. 7. pp. 1314-1324.

H. R. Hong, J. Kim, and C. H. Park, "Facile fabrication of multifunctional fabrics: use of copper and silver nanoparticles for antibacterial, superhydrophobic, conductive fabrics," RSC Adv., vol. 8, no. 73, pp. 41782-41794, 2018.
https://doi.org/10.1039/C8RA08310J

M. M. Jolaei, M. Montazer, A. S. Rashidi, and M. B. Moghadam, "Green synthesis copper nano particles for increasing antibacterial properties of polyester fabrics," Res. J. Pharm. Biol. Chem. Sci., 2016.

J. Lim, S. P. Yeap, H. X. Che, and S. C. Low, "Characterization of magnetic nanoparticle by dynamic light scattering," Nanoscale Res. Lett., vol. 8, no. 1, p. 381, Sep. 2013.
https://doi.org/10.1186/1556-276X-8-381

A. Nasirian, "Synthesis and characterization of {Cu} nanoparticles and studying of their catalytic properties," Int. J. Nano Dimens., vol. 2, no. 3, pp. 159-164, Mar. 2012.

H. Zhao, T. Liang, and B. Liu, "Synthesis and properties of copper conductive adhesives modified by SiO2 nanoparticles," Int. J. Adhes. Adhes., 2007.
https://doi.org/10.1016/j.ijadhadh.2006.03.006

X. Song, S. Sun, W. Zhang, and Z. Yin, "A method for the synthesis of spherical copper nanoparticles in the organic phase," J. Colloid Interface Sci., 2004.
https://doi.org/10.1016/j.jcis.2004.01.019
Publicado
2020-12-01
Cómo citar
Mahdi Jolaei, M., Montazer, M., Rashidi, A.-S., & Bameni Moghadam, M. (2020). Modificación de tejido de poliéster mediante la fabricación de compuestos de nano-cobre. Revista Innovaciencia, 8(1), 1-12. https://doi.org/10.15649/2346075X.1005
Sección
Artículo de investigación científica y tecnológica